Malleable iron pipe fittings internal control method

First, the most factors touching the treatment impact

Mary pipe items coping with the correct quantity thanks to its vary of geological process component needs terribly slender, and so tougher to stabilize than ductile iron. this needs that the relevant method factors should attempt to try and do less volatility. Treatment impact of malleable iron pipe fittings larger method factors square measure primarily the subsequent aspects.

black malleable iron pipe fittings in china

1, the sulfur content of the initial hot metal


Elemental sulfur consumption deterioration. it's a awfully strong interaction of hot metal sulfur and high metallic element, cerium, calcium, there square measure a lot of modifier is cured into the dross, thereby reducing the power to cause deterioration of unsuccessful treatment. Therefore, within the production of malleable iron pipe fittings ought to attempt to use low sulfur-containing iron and coke. Conditions, take advance measures for desulphurization is helpful. this is often to not say that with the next sulfur content of the liquid iron cannot be with success processed malleable iron pipe fittings. several domestic and foreign factories with a sulfur content of up to zero.06-0.08% of hot metal cupola may be stably created malleable iron pipe fittings, however deterioration of the alloy to be employed in Associate in Nursing quantity a lot of. info on experiences with zero.07-0.13% sulfur hot metal production of compacted carbon forged iron that below sure conditions, like atomic number 22 to expand the scope of action from the employment of anti-ball impact of sulfur. even so, the number of sulfur is stable process malleable iron pipe fittings necessary necessities.

2, the process temperature of liquid iron


When the liquid iron temperature treatment United States Government Accounting Office had a major impact on the absorption rate of the alloy, particularly magnesium-based vermicularizing even a lot of therefore. the upper the temperature, the a lot of violent boiling metallic element chemical process, burning the a lot of less, some as low as potential so the process temperature furthermore. Document describes once mistreatment metallic element atomic number 22 composite modifier process malleable iron pipe fittings, the results of various treatment temperature on treatment potency. process at 1400 ℃, the worm-like carbon in additional than ninety fifth, the ball rarely; at 1280 ℃ treatment, over half the carbon nodules. Alloy quantity is that the same, the process temperature of the massive visible absorption rate.
In actual production, the temperature should be thought of to work out the method for casting gushing temperature necessities. However, the process temperature should be as stable as potential, if the temperature fluctuation is massive, the number should be adjusted alloy, otherwise it's troublesome to confirm the standard of treatment.
Rare earth-based vermicularizing, the process temperature is higher well, the temperature is just too low isn't straightforward even, not even totally fusible alloy, so touching the treatment impact.
3. process operations
Since the creep method of the method because of fluctuations in response tangled sensitive, so requiring operation suggested to strictly correct. Uniformity of the alloy composition, alloy covering the case, quantitative and iron alloys, dross dross and different measures, like have an immediate impact on the treatment impact.

Our company as a Malleable iron pipe fittings supplier ,if you need that pls contact us.
Contact Us
  • +86-311-68019517
  • bonny@archpipe.com
  • Malleable Iron Zone,Shijiazhuang City,Hebei Province
facebook twitter pinterest linkedin
Message
*Name
*Tel
*E-mail
*Message
Copyright SHIJIAZHUANG JIZHONG MALLEABLE IRON CO.,LTD. All rights reserved.
Online Service×
Middle East& Southeast Asia
Contact : Tina-Zhang Tel : +86-311-68019537 Mobile : 0086-18230416770 E-mail : salestina@archpipe.com Whatsapp : +86-18230416770 Skype : fenghongmei8112
South America &Russia
Contact : Sophia-Zhang Tel : +86-311-68019537 Mobile : 0086-18230416760 E-mail : salessophia@archpipe.com Whatsapp : +86-18230416760 Skype : jizhong20062007
South Africa & Australia
Contact : Hellen-Wang Tel : +86-311-68019537 Mobile : 0086-13832355261 E-mail : saleshellen@archpipe.com Whatsapp : +86-13832355261 Skype : hellen136926